Any process of deterioration and consequent loss of a solid metallic material, through an unwanted chemical or electrochemical attack by its environment, starting at its surface, is called corrosion.
PASSIVITY
• Passivity is a phenomenon by which a metal exhibits corrosion resistance
• It is the result of formation of a highly protective, but very thin and invisible film on the surface of the metal.
Causes of corrosion in RC structures
Ø Carbonation
Ø Chloride attack
Ø Carbonation
• Reduction of pH in cover concrete which causes loss of passive oxide layer
• Low pH caused by reaction of Calcium Hydroxide (Ca(OH))2 in concrete with atmospheric Carbon Dioxide
Ø CHLORIDE ATTACK
• Caused by chlorides breaking up passive oxide layer
• The moisture in concrete pores will act as electrolyte, and the area adjacent to concentration of chloride ions on the reinforcement steel will become cathode initiates corrosion.
Principle of corrosion
• when there is difference in electrical potential along the steel reinforcement, an electrochemical cell is set up.
• One part of the steel becomes anode and other becomes cathode and the pore water acts as an electrolyte.
• these positively charged ferrous ions at the anode passes into solution
• the negatively charged free electron passes through the steel into cathode
• They are absorbed by the constituent of electrolyte and combine with water and oxygen to form hydroxyl ions
• These hydroxyl ions combine with ferrous ions to form ferrous hydroxide which is further oxidized to ferric hydroxide
Prevention in new structure
• Corrosion can be controlled during construction by enhancing the quality of the material used and adjusting to the local environment.
The following approaches are commonly used:
– Corrosion inhabiting admixtures
– Coating to reinforcement
– Coating to concrete surface
Corrosion inhabiting admixtures
• Use of corrosion inhabiting admixtures such as Nitrates, Phosphates, and Benzoates can prevent or delay corrosion.
typical dosage : 10 – 30 lts/m3 of concrete
Coating to reinforcement
• Steel can be made more corrosion resistant by altering its structure through metallurgical process.
Ø Material used for coating Epoxy
Ø zinc
Ø Epoxy coating:
• The bar in the plant heated to a controlled temperature, epoxy powder are deposited evenly on the surface of the bar.
Galvanized coating:
• Dipping the steel bars in molten zinc, these results in a coating of zinc bonded to the surface of steel.
Coating to concrete:
• The protective coatings are based on acrylics Such as Silicones, chlorinated rubber, epoxy phenol which retains the breathing property of concrete.
• Coating used in the concrete serve the dual purpose of protection and decoration, increases clean ability by reducing dust.
Rehabilitation of corroded structure
Electrochemical treatment of concrete is becoming more popular as a repair and restoration option to stop corrosion and extend the service life of existing RC structures.
Ø Electrochemical methods:
– realkalisation
– chloride extraction
Realkalisation
• used in carbonation induced corrosion
Chloride extraction
• used in treatment of chloride induced corrosion
Electrochemical chloride extraction:
• Removes chlorides from concrete by ion migration
• Regenerates the protective passive layer around the reinforcing steel
Mechanism:
• An anode is embedded in an electrolyte media is applied to the surface of the concrete.
• The cathode is connected to reinforcing steel in the concrete
• The two terminals are connected to a DC power supply
• chloride ions being negative migrate towards the positive electrode, the anode.
• Since this is external to the concrete, the chloride content of the concrete is reduced particularly on and around the negatively charged reinforcing steel.
• Simultaneously the electrolytic production of hydroxyl ions at the reinforcing steel surface results in a high pH being generated around the steel.
• Thus concrete becomes chloride free and high alkaline concrete
Advantages:
• Non-destructive repair method
• Removes the cause of corrosion
• Architectural and exposed aggregate finishes can be maintained
• No need of expensive structural support
• Lower cost
• Extended service life
• Fast installation and removal
• No permanent maintenance required
• More environmentally friendly
Conclusion:
• Corrosion being one of the major problem for deterioration of concrete the solution for this is also based on the principles of chemical reaction and electricity.
• The ultimate aim is to solve the problem of corrosion to increase the durability of concrete structures.
• Selection of any system of prevention , protection and remedial measures will depend on the case and exposure conditions of concrete during its service life